S275JR Structural Steel Plate Stockist in India As Per EN 10025-2:2004
Table Of Content
- S275JR Plate Specification
- Mild Steel S275JR Plate Thickness Tolerance
- Equivalent Of S275JR Steel Plates
- Weight Of EN 10025-2 S275JR Structural Steel Plate
- EN 10025-2 S275JR Plate Chemical Composition
- Difference Between S275jr and S355jr
- Application Of S275JR High Tensile Steel Plate
- S275JR Structural Steel Plate Sizes
- Mechanical Properties Of S275JR Mild Steel Plate
- Types Of S275JR Pressure Vessel Plate
- S275 High Strength Structural Steel Plates Testing
- Authorised Manufacturer Of S275JR Carbon Steel Plate
- S275JR Hot Rolled Structural Steel Plate Impact Test
S275JR Plate Stockist in India in Custom Sizes For Structural Application
| Standard | EN 10025-2:2004 |
|---|---|
| Width | 1000mm-4500mm |
| Thickness | 5mm-150mm |
| Length | 3000mm -18000mm |
| Hardness | As per NACE MR 175 |
| Welding | Can be welded without limitations |
| Impact tested | -52° C |
| Classification | Non-alloy structural steel. |
| Processing | Welding, Cutting, Drilling, Bending Etc. |
| Process | Hot-Rolled (HR) |
| Delivery State | AR, HR, N |
| Surface Finish | Anti Rust Oiled, Pe Coated, Anti Rust Varnished, Galvanized, Color Coated, Black Painted |
| TPI | BV, SGS, Intertek, etc. |
| Packaging | Plastic Bags, Wooden Boxes |
| Origin | Indian, Japanese, Korean, USA, Russian, European, Ukraine |
Supplier Of S275JR Carbon Steel Hot Rolled Plate With Impact Tested At -52° C in Mumbai, Refer Thickness Tolerance
| Thickness (T) mm S275JR | |||||
|---|---|---|---|---|---|
| Tolerance band | |||||
| ≤ 1200 | > 1200 ≤ 1500 | > 1500 ≤ 1800 | |||
| > 2.5 ≤ 3.0 | ±0.20 | > 2.5 ≤ 3.0 | ±0.22 | ||
| > 2.0 ≤ 2.5 | ±0.18 | > 2 ≤ 2.5 | ±0.21 | ||
| > 4.0 ≤ 5.0 | ±0.24 | > 4.0 ≤ 5.0 | ±0.26 | > 4.0 ≤ 5.0 | ±0.28 |
| > 3.0 ≤ 4.0 | ±0.22 | > 3.0 ≤ 4.0 | ±0.24 | > 3.0 ≤ 4.0 | ±0.26 |
| > 5.0 ≤ 6.0 | ±0.26 | > 5.0 ≤ 6.0 | ±0.28 | > 5.0 ≤ 6.0 | ±0.29 |
| > 8.0 ≤ 10.0 | ±0.32 | > 8.0 ≤ 10.0 | ±0.33 | > 8.0 ≤ 10.0 | ±0.34 |
| > 6.0 ≤ 8.0 | ±0.29 | > 6.0 ≤ 8.0 | ±0.30 | > 6.0 ≤ 8.0 | ±0.31 |
| > 10.0 ≤ 12.5 | ±0.35 | > 10.0 ≤ 12.5 | ±0.36 | > 10.0 ≤ 12.5 | ±0.37 |
Buy S275JR High Tensile Steel Plate in Maximum Sizes Online With Various Surface Finish, Refer Equivalent and Weight
| EN | UNI | JIS | DIN,WNr | IS | AFNOR | ISO | ASTM |
|---|---|---|---|---|---|---|---|
| S275JR | Fe430B | SS400 | RSt42-2 St 44-2 |
IS2062 | E28-2 | E275B | A283D A529 Gr.D |
| France | E28-2 |
| Germany | St44-2 |
| UK | 43B |
| Sweden | 1412-00 |
| Europe (outdated) | Fe430B |
| Norway | NS12142 |
| LxW (mm) | T (mm) | Kg/e |
|---|---|---|
| 2000 x 1000 | 4.0 | 62.8 |
| 2.0 | 31.4 | |
| 1.5 | 23.6 | |
| 3.0 | 47.1 | |
| 6.0 | 94.2 | |
| 5.0 | 78.5 | |
| 10.0 | 157.0 | |
| 8.0 | 125.6 | |
| 3000 x 1500 | 6.0 | 212.0 |
| 4.0 | 141.3 | |
| 3.0 | 106.0 | |
| 5.0 | 176.6 | |
| 10.0 | 353.3 | |
| 8.0 | 282.6 | |
| 2500 x 1250 | 4.0 | 98.1 |
| 2.0 | 49.1 | |
| 1.5 | 36.8 | |
| 3.0 | 73.6 | |
| 6.0 | 147.2 | |
| 5.0 | 122.7 | |
| 10.0 | 245.3 | |
| 8.0 | 196.3 | |
| 12.0 | 294.4 |
| C for nominal thickness in mm | Mn | P | S | N | Cu | ||
|---|---|---|---|---|---|---|---|
| ≤ 16 | ˃16 ≤ 40 | ˃ 40 | |||||
| ≤ 0.21 | ≤ 0.21 | ≤ 0.22 | ≤ 1.50 | ≤ 0.035 | ≤ 0.035 | ≤ 0.012 | ≤ 0.55 |
Exporter and Stockholder Of S275JR Mild Steel Plate, Understand Difference Between S275jr and S355jr Here
| Property | S275JR | S355JR |
|---|---|---|
| Tensile Strength | 430-550 MPa | 470-630 MPa |
| Machinability | Generally good | Generally Good Due to Higher Strength May Require More Careful Handling |
| Yield Strength | 275 MPa (minimum) | 355 MPa (minimum) |
| Chemical Composition | Higher Manganese, Lower Carbon Content | Balanced Manganese and Silicon, Slightly Higher Carbon Content, |
| Elongation | 26% | 22% |
| Applications | Where Lower Strength is Acceptable Like General Construction, Structural Applications | Requiring Higher Strength and Better Toughness Like More Demanding Structural Applications |
| Weldability | Good | Good, Due to Higher Strength More Stringent Control Needed |
Get S275JR Pressure Vessel Plate From Genuine Dealer and Distributors For Structural Application
- Tanks
- Engineering
- Construction
- Yellow goods
- Bridges
- Rail
- Energy
| Standard sheet sizes | ||||||
|---|---|---|---|---|---|---|
| mm | mm | mm | mm | mm | mm | |
| 1000 | 1250 | 2000 | 2500 | 3000 | 1500 | |
| 2000 | 4000 | |||||
| Nominal thickness, mm | Strength limit, MPa | Minimum yield strength, MPa |
|---|---|---|
| ≥3 ≤ 16 | 410-560 | 275 |
| <3 | 430-580 | 275 |
| > 16 ≤ 40 | 410-560 | 265 |
| > 63 ≤ 80 | 410-560 | 245 |
| > 250 ≤ 400 | 380-540 | 195 |
| > 40 ≤ 63 | 410-560 | 255 |
| > 80 ≤ 100 | 410-560 | 235 |
| > 150 ≤ 200 | 380-540 | 215 |
| > 100 ≤ 150 | 400-540 | 225 |
| > 200 ≤ 250 | 380-540 | 205 |
Types Of S275JR Pressure Vessel Plate
S275jr Hot Rolled Carbon Steel Plate
S275jr Chequered Steel Plate
S275jr Mild Steel Plate
20mm 25mm 50mm 60mm S235jr Carbon Steel Plate
S275jr Pressure Vessel Plate
S275jr Carbon Wear Resistant Steel Plate
| Destructive Tests | Non Destructive Tests |
|---|---|
|
|
ESSAR
NIPPON STEEL
SSAB
JFE
SALZGITTER
JINDAL
APERAM
ACRONI
POSCO
| Minimum elongation - A | Notch impact test | ||||||
|---|---|---|---|---|---|---|---|
| Lo = 5,65 * √So (%) | |||||||
| Nominal thickness | Min. absorbed energy |
Temperature | |||||
| mm | |||||||
| >100 | >40 | >3 | >63 | >250 | >150 | J | °C |
| ≤150 | ≤63 | ≤40 | ≤100 | ≤400 | ≤250 | ||
| 19 | 22 | 23 | 21 | - | 18 | 27 | 20 |
Check Countrywise Shipping Time
| Export to | Shipping Time | Price Variations |
|---|---|---|
| South Africa | 25-30 | 5 % extra |
| UAE | 5 days | |
| Saudi Arabia | 7 | |
| USA | 40-60 | |
| Qatar | 7 | |
| Uk | 30 | |
| Italy | 30 | |
| France | 30 | |
| Malaysia | 10 | |
| Indonesia | 9 | |
| Philippines | 14 | |
| Oman | 5 | |
| Kuwait | 10 | |
| Bahrain | 9 | |
| Singapore | 8 |