2219-T62 Aluminum Sheet Supplier, Get custom sizes and cut to length Aluminum Alloy 2219 Plate at best price Ex Mumbai
We at triton specialize in 2219-T851 Aluminum Plate, We provide the best quality range of 2219 Aluminum Sheet material
Table Of Content
The 2219 aluminum is an age-hardenable alloy grade. A 2219 Aluminum Plate is designed with a chemical composition of aluminum as the primary element with copper, manganese, zirconium, vanadium, and titanium. The content embedded in these modules gives them enhanced strength and moderate corrosion resistance properties. 2219 Aluminum Alloy Plate provides stability to different applications. These plates work well in low-temperature setups and moderately high-temperature applications.
The Aluminum 2219 Plate has a density of 2.8 g/cm3 with a melting point of 510 degrees C. These plates have a minimum tensile strength of 170mpa with a minimum yield strength of 76mpa. The Aluminum Alloy 2219 Plate has an elastic modulus between 70-80Gpa and has a fatigue strength of 105mpa. These plates can be easily elongated by 18% in the system.
The 2219-t851 Aluminum Plate tempers are recognized variations of the plate that are designed to either increase their strength or the dimensional accuracy of the module. Similar to this is the 2219-t852 Plate. Here a special material is added to the plate as the casting cools down to ensure higher strengths. The 2219-t87 Plate is tempered to attain exceptional strengths. These plates are subjected to higher cold-forming properties that are beyond flattening or straightening. 2219-t81 Plate is tempered to meet the dimensional accuracy and stress relief across different setups. The temper of the 2219-t6 Plate can be customized to meet specific product requirements.
These plates can be easily produced in different sizes and shapes to suit different applications. The 2219 Aluminum Sheet is slightly thinner than a plated metal. These sheets add an aesthetical appeal to different components and don’t really work well in applications requiring strength and stability. A 2219-t62 Aluminum Sheet is tempered by solution heat treatment processes and artificially aged till it can meet standard mechanical properties. A 2219-t31 Plate can be easily customized as per requirements.
We are a certified distributor of Aluminum 2219 Plate in various specifications available in various form
Temper |
Alloy |
Width |
Thickness |
T6 (CS) |
2219 |
1200-3800mm |
4-260mm |
T62 (MCS) |
2219 |
1200-3800mm |
4-260mm |
T87/C10S |
2219 |
1200-3800mm |
4-260mm |
- Temper: 2219-T31, 2219-0, 2219-T37, 2219-T81, 2219-T87
- MIL-A-46118, ASTM-B-316, ASTM-B-211, MIL-A-46808, ASTM-B-209, MIL-A-8920, ASTM-B-221 (Plates)
- 2219-T851, 2219-T351
- Clad: AMS 4095, AMS 4094, DMS-1719, AMS 4096, BMS-7-110
- As per AMS-QQ-A250/3 2219-T851 Aluminum Plates
- Bare: AMS 4031, QQ-A-250/30
A copper addition is used to make Aluminium Alloy 2219, an age-hardenable alloy. It's famous for its structural strength, and it's employed in a variety of high-temperature applications. forming, Machining, heat treatment, cold working, and other metalworking techniques are all possible with this alloy. When compared to the other 2219 aluminium versions, it has the lowest ductility. 2219 Aluminum alloy is a high-strength, heat-resistant aluminium alloy that may be utilised as working components below. In terms of thermal state, annealing, and quenching conditions, it is more formable.
Description | Price |
Aluminum Alloy Plates 2219-T851 | US $ 2900-3400 / Ton |
2219 4X8 Feet Alloy Mirror Aluminum Plates for Mold | US $ 3660-3880 / Piece |
Midle Thick 2219 Aluminum Sheet | US $ 2500-4500 / Ton |
Aerospace Materials 2219 Aluminium Alloy Plates | US $ 2000-4000 / Ton |
2219 Free Cutting 2mm 3mm T6 Aluminum Alloy Plates | US $ 2377.95-2440.94 / Ton |
30X1500X3000mm 2219 Forged T651 T6 Aluminum Alloy Plates | US $ 2-4 / kg |
2219 Aluminium Sheet/Plates | US $ 1800-2500 / Ton |
2219 Aluminium Plates Sheet | US $ 1800-2600 / Ton |
0.2-300mm Thcikness 2219 Aluminum Plates | US $ 1800-2200 / Ton |
offer a broad range of 2219-t852 Plate through a worldwide network in compliance with international standards

2219 Aluminum Plates

2219-T62 Aluminum Sheet

2219 Aluminum Sheet

2219-T851 Aluminum Plates

Aluminum Alloy 2219 Plates

2219-T852 Plate
|
|
Property | Imperial | Metric |
---|---|---|
Melting Point | 1010-1190°F | 543 – 643 °C |
Density | 0.103 lb/in3 | 2.84 g/cm3 |
Specific Heat Capacity | 0.207 BTU/lb-°F | 0.864 J/g-°C |
Product Categories |
Heat Treatment |
Width(mm) |
Thickness(mm) |
Length(mm) |
Hot-Rolled Thick plates |
H112 |
≤1350 |
8~200 |
≤9000 |
≤1350 |
8~200 |
|||
≤1250 |
8~10 |
|||
≤1250 |
8~10 |
|||
≤1350 |
10~200 |
|||
≤1200 |
8~10 |
|||
≤1350 |
10~200 |
|||
≤1000 |
8~10 |
|||
≤1250 |
10~15 |
|||
≤1350 |
15~200 |
|||
≤1350 |
15~200 |
Product Categories |
Coil Weight(t) |
Width(mm) |
Thickness(mm) |
Length(mm) |
Heat Treatment |
Cold-Rolled |
<6(width:50mm~800mm,thickness:0.2~0.6mm) |
≤1340 |
0.2~3.5 |
≤6000 |
O, H12/22, H14/24, H16/26, H18, H32, H34, H36, H38 |
≤1250 |
|||||
≤1251 |
|||||
≤1252 |
|||||
≤1253 |
|||||
≤1254 |
|||||
≤1255 |
|||||
≤1256 |
Aluminium Alloy 2219 SHEET IN STOCK |
|||
Aluminium ALLOY | COND. | TEMPER | SIZE |
2219 | BARE | T81 | .020" X 48" X 144" |
2219 | BARE | T31 | .020" X 48" X 144" |
2219 | BARE | T81 | .025" X 48" X 144" |
2219 | CLAD | T31 | .025" X 48" X 144" |
2219 | BARE | T81 | .032" X 48" X 144" |
2219 | CLAD | T31 | .032" X 48" X 144" |
2219 | BARE | T81 | .040" X 48" X 144" |
2219 | CLAD | O | .040" X 48" X 144" |
2219 | BARE | O | .040" X 48" X 144" |
2219 | CLAD | T31 | .040" X 48" X 144" |
2219 | CLAD | T81 | .050" X 48" X 144" |
2219 | CLAD | O | .050" X 48" X 144" |
2219 | BARE | T81 | .050" X 48" X 144" |
2219 | CLAD | T31 | .063" X 48" X 144" |
2219 | CLAD | T31 | .050" x 48" x 144" |
2219 | CLAD | T81 | .063" X 48" X 144" |
2219 | BARE | T81 | .063" X 48" X 144" |
2219 | BARE | O | .063" X 48" X 144" |
2219 | CLAD | O | .071" X 48" X 144" |
2219 | CLAD | T31 | .071" X 48" X 144" |
2219 | CLAD | O | .063" X 48" X 144" |
2219 | CLAD | O | .080" X 48" X 144" |
2219 | BARE | T31 | .080” X 48” X 144” |
2219 | CLAD | T31 | .080" X 48" X 144" |
2219 | CLAD | T81 | .080” X 48” X 144” |
2219 | CLAD | O | .090" X 48" X 144" |
2219 | CLAD | T31 | .090" X 48" X 144" |
2219 | CLAD | T31 | .100" X 48" X 144" |
2219 | CLAD | T31 | .125" X 48" X 144" |
2219 | BARE | T81 | .100" X 48" X 96" |
2219 | CLAD | T81 | .125" X 48" X 144" |
2219 | BARE | T81 | .125" X 48" X 144" |
2219 | BARE | O | .125" X 48" X 144" |
At Triton we have 20 years of experience supplying 2219-T81/ T87 Plate and more to your custom measurements and shapes.
Dimensions |
||||||||
240 |
210 |
200 |
230 |
330 |
310 |
300 |
320 |
315 |
370 |
350 |
340 |
360 |
410 |
385 |
380 |
400 |
390 |
450 |
430 |
420 |
440 |
490 |
470 |
460 |
480 |
475 |
530 |
505 |
500 |
520 |
580 |
550 |
540 |
570 |
560 |
620 |
600 |
590 |
610 |
670 |
640 |
630 |
660 |
650 |
710 |
690 |
680 |
700 |
770 |
735 |
720 |
760 |
750 |
810 |
790 |
780 |
800 |
880 |
830 |
820 |
860 |
840 |
Heat treatment of aluminum/aluminum 2219 alloy at 538°C (1000°F) followed by quenching in cold water is possible.
Chemical Composition |
|||||||||
Weight % | Cu | Si | Al | Fe | Mg | Mn | Ti | Zn | Others |
2219 |
5.80-6.80 | 0.20 max | Bal | 0.30 max | 0.02 max |
0.20-0.40 | 0.02-0.10 |
0.10 max | 0.050 ea 0.15 Total |
(Bare) Aluminium 2219 - Sheet / Plate
Material | Yield Strength ksi | Elongation in 2" (%) | Thickness | Temper | Tensile Strength ksi |
Alloy 2219 (QQ-A-250/30) | 28 | 10 | 0.250" - 2.00" | T351 | 46 |
Alloy 2219 (QQ-A-250/30) | 16 max | 12 | 0.020"-2.00 | 0 | 32 max |
Alloy 2219 (QQ-A-250/30) | 46 | 7-8 | 0.250" - 2.00" | T851 | 62 |
Temper T81 / T851 Aluminium 2219 - Sheet / Plater (Clad)
Material | Yield Strength ksi | Thickness | Temper | Tensile Strength ksi | Elongation in 2" (%) |
2219 (AMS 4094) | 42 | 0.245"-0.499" | T81/ T851 | 58 | 8 |
Alloy 2219 (AMS 4094) | 41 | 0.039"-0.099" | T81/ T851 | 55 | 7 |
Alloy 2219 (AMS 4094) | 37 | 0.020"-0.039" | T81/ T851 | 49 | 6 |
Alloy 2219 (AMS 4094) | 43 | 0.099"-0.249" | T81/ T851 | 58 | 7 |
- Space boosters
- Structural members
- Supersonic aircraft skin
- High strength weldments
- Aircraft parts
- Fuel tanks
Property | Imperial | Metric |
---|---|---|
CTE, linear 250°C | 13.4 µin/in-°F | 24.1 µm/m-°C |
Liquids | 1190 °F | 643 °C |
CTE, linear 68°F | 12.4 µin/in-°F | 22.3 µm/m-°C |
Thermal Conductivity | 833 BTU-in/hr-ft²-°F | 120 W/m-K |
Specific Heat Capacity | 0.207 BTU/lb-°F | 0.864 J/g-°C |
Solidus | 1010°F | 543°C |